DONATE

Publications

by Keyword: biodegradable metals

García-Mintegui, C, Chausse, V, Labay, C, Mas-Moruno, C, Ginebra, MP, Cortina, JL, Pegueroles, M, (2024). Dual peptide functionalization of Zn alloys to enhance endothelialization for cardiovascular applications Applied Surface Science 645, 158900

A new generation of fully bioresorbable metallic Zn-based alloys could be used for stenting applications; however, the initial surface degradation delays stent re-endothelialization. Thus, this work proposes a dual strategy to control the corrosion and accelerate the endothelialization of ZnMg and ZnAg biodegradable alloys. First, a stable polycaprolactone (PCL) coating is obtained and followed by its functionalization with either linear RGD (Arg-Gly-Asp) or REDV (Arg-Glu-Asp-Val) peptides or a dual peptide-based platform combining both sequences (RGD-REDV). Scratching tests showed neither delamination nor detachment of the polymeric coating. Potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS) measurements confirmed the corrosion resistance after PCL coating by revealing lower current density and higher absolute impedance values. X-ray photoelectron spectroscopy (XPS) and fluorescent microscopy confirmed the correct peptide immobilization onto PCL coated Zn alloys. The functionalized samples exhibited enhanced human umbilical vein endothelial cells (HUVEC) adhesion. The higher number of adhered cells to the functionalized surfaces with the RGD-REDV platform demonstrates the synergistic effect of combining both RGD and REDV sequences. Higher corrosion resistance together with enhanced endothelialization indicates that the dual functionalization of Zn alloys with PCL and peptide-based RGD-REDV platform holds great potential to overcome the clinical limitations of current biodegradable metal stents.

JTD Keywords: Biodegradable metals, Cell adhesive peptides, Corrosion, Degradation, Dual peptide-based platform, Endothelialization, Functionalization, In-vitro, Magnesium alloys, Mg alloy, Polycaprolactone coating, Polymer-coatings, Rgd-functionalization, Surface, Zinc, Zinc alloys


García-Mintegui C, Córdoba LC, Buxadera-Palomero J, Marquina A, Jiménez-Piqué E, Ginebra MP, Cortina JL, Pegueroles M, (2021). Zn-Mg and Zn-Cu alloys for stenting applications: From nanoscale mechanical characterization to in vitro degradation and biocompatibility Bioactive Materials 6, 4430-4446

In the recent decades, zinc (Zn) and its alloys have been drawing attention as promising candidates for bioresorbable cardiovascular stents due to its degradation rate more suitable than magnesium (Mg) and iron (Fe) alloys. However, its mechanical properties need to be improved in order to meet the criteria for vascular stents. This work investigates the mechanical properties, biodegradability and biocompatibility of Zn-Mg and Zn-Cu alloys in order to determine a proper alloy composition for optimal stent performance. Nanoindentation measurements are performed to characterize the mechanical properties at the nanoscale as a function of the Zn microstructure variations induced by alloying. The biodegradation mechanisms are discussed and correlated to microstructure, mechanical performance and bacterial/cell response. Addition of Mg or Cu alloying elements refined the microstructure of Zn and enhanced yield strength (YS) and ultimate tensile strength (UTS) proportional to the volume fraction of secondary phases. Zn-1Mg showed the higher YS and UTS and better performance in terms of degradation stability in Hanks’ solution. Zn-Cu alloys presented an antibacterial effect for S. aureus controlled by diffusion mechanisms and by contact. Biocompatibility was dependent on the degradation rate and the nature of the corrosion products.

JTD Keywords: behavior, biocompatibility, biodegradable metals, bioresorbable metals, bioresorbable scaffold, copper, corrosion properties, elastic-modulus, galvanic corrosion, microstructure, nanoindentation, redox homeostasis, zinc, Biocompatibility, Bioresorbable metals, Galvanic corrosion, Nanoindentation, Room-temperature superplasticity, Zinc alloys