The efficiency of synthetic bone grafts can be evaluated either in osseous sites, to analyze osteoconduction or ectopically, in intramuscular or subcutaneous sites, to assess osteoinduction. Bone regeneration is usually evaluated in terms of the presence and quantity of newly formed bone, but little information is normally provided on the quality of this bone. Here, we propose a novel approach to evaluate bone quality by the combined use of spectroscopy techniques and nanoindentation. Calcium phosphate scaffolds with different architectures, either foamed or 3D-printed, that were implanted in osseous or intramuscular defects in Beagle dogs for 6 or 12 weeks were analyzed. ATR-FTIR and Raman spectroscopy were performed, and mineral-to-matrix ratio, crystallinity, and mineral and collagen maturity were calculated and mapped for the newly regenerated bone and the mature cortical bone from the same specimen. For all the parameters studied, the newly-formed bone showed lower values than the mature host bone. Hardness and elastic modulus were determined by nanoindentation and, in line with what was observed by spectroscopy, lower values were observed in the regenerated bone than in the cortical bone. While, as expected, all techniques pointed to an increase in the maturity of the newly-formed bone between 6 and 12 weeks, the bone found in the intramuscular samples after 12 weeks presented lower mineralization than the intraosseous counterparts. Moreover, scaffold architecture also played a role in bone maturity, with the foamed scaffolds showing higher mineralization and crystallinity than the 3D-printed scaffolds after 12 weeks.

JTD Keywords: Atr-ftir, Bone regeneration, Calcium-phosphate, Ectopic implantation, Implant interface, In-vivo, Indentation, Mechanical-properties, Micromechanical properties, Nanoindentation, Orthotropic implantation, Raman spectroscop, Raman-spectroscopy, Strengt, Substitutes

Porous zirconia scaffolds manufactured using polymer-infiltrated ceramic network (PICN) and additive manufacturing technologies are emerging as promising alternatives to traditional ceramic materials in dental restorations. However, incomplete osseointegration and bacterial infections still represent challenges for the long-term performance of this new composite material. To address this, the present study aims to investigate the effect of peptide biofunctionalization on the biological performance of infiltrated zirconia scaffold surfaces. The samples used in the work consisted of a 3D-printed zirconia scaffold infiltrated with a dimethacrylate copolymer. Surface biofunctionalization was achieved using a synthetic platform containing the cell-adhesive sequence RGD and the antibacteria LF1-11 peptide (RGD-LF). The attachment of the molecule was characterized through fluorescence confocal laser scanning microscopy and X-ray photoelectron spectroscopy. The biological performance of the samples was evaluated in terms of human mesenchymal stem cell adhesion and early attachment of S. aureus. The physicochemical characterization verified the successful anchoring of the biomolecule to the surface, leading to a peptide density of 288 pmol/cm2. 2 . The biological assays confirmed the potential of RGD-LF to improve cell adhesion and spreading. In this sense, the average cell area increased fourfold in the biofunctionalized surface. Regarding bacterial adhesion, it was demonstrated that RGD-LF significantly inhibited it, reducing early adhesion by half compared to the untreated surface. Overall, this study provides valuable insights into the biofunctionalization of polymer-infiltrated 3D scaffolds for the development of cell-instructive and antibacterial surfaces tailored for dental applications.

JTD Keywords: Antibacteria, Biocompatibility, Cell adhesion, Composite, Dental ceramics, Direct ink writing, Fabrication, Infiltrated zirconia scaffolds, Mechanical-properties, Peptide biofunctionalization, Picn material, Strength, Surface, Topograph, Wear behavior

Steroid myopathy is a clinically challenging condition exacerbated by prolonged corticosteroid use or adrenal tumors. In this study, we engineered a functional three-dimensional (3D) in vitro skeletal muscle model to investigate steroid myopathy. By subjecting our bioengineered muscle tissues to dexamethasone treatment, we reproduced the molecular and functional aspects of this disease. Dexamethasone caused a substantial reduction in muscle force, myotube diameter and induced fatigue. We observed nuclear translocation of the glucocorticoid receptor (GCR) and activation of the ubiquitin-proteasome system within our model, suggesting their coordinated role in muscle atrophy. We then examined the therapeutic potential of taurine in our 3D model for steroid myopathy. Our findings revealed an upregulation of phosphorylated AKT by taurine, effectively countering the hyperactivation of the ubiquitin- proteasomal pathway. Importantly, we demonstrate that discontinuing corticosteroid treatment was insufficient to restore muscle mass and function. Taurine treatment, when administered concurrently with corticosteroids, notably enhanced contractile strength and protein turnover by upregulating the AKT-mTOR axis. Our model not only identifies a promising therapeutic target, but also suggests combinatorial treatment that may benefit individuals undergoing corticosteroid treatment or those diagnosed with adrenal tumors.

JTD Keywords: 3d bioengineered skeletal muscle tissues, Adrenal cortex hormones, Atroph, Colocalization, Corticosteroids, Dexamethasone, Glucocorticoid-receptor, Humans, Mechanisms, Models, biological, Mtor protein, human, Muscle contraction, Muscle fibers, skeletal, Muscle strength, Muscle, skeletal, Muscular diseases, Organ size, Phosphorylation, Proteasome endopeptidase complex, Proto-oncogene proteins c-akt, Receptors, glucocorticoid, Signal transduction, Skeletal-muscle, Steroid myopathy, Steroids, Supplementation, Taurin, Taurine, Tor serine-threonine kinases, Ubiquitin

The application of 3D printing to calcium phosphates has opened unprecedented possibilities for the fabrication of personalized bone grafts. However, their biocompatibility and bioactivity are counterbalanced by their high brittleness. In this work we aim at overcoming this problem by developing a self -hardening ink containing reactive ceramic particles in a polycaprolactone solution instead of the traditional approach that use hydrogels as binders. The presence of polycaprolactone preserved the printability of the ink and was compatible with the hydrolysis -based hardening process, despite the absence of water in the ink and its hydrophobicity. The microstructure evolved from a continuous polymeric phase with loose ceramic particles to a continuous network of hydroxyapatite nanocrystals intertwined with the polymer, in a configuration radically different from the polymer/ceramic composites obtained by fused deposition modelling. This resulted in the evolution from a ductile behavior, dominated by the polymer, to a stiffer behavior as the ceramic phase reacted. The polycaprolactone binder provides two highly relevant benefits compared to hydrogel-based inks. First, the handleability and elasticity of the as -printed scaffolds, together with the proven possibility of eliminating the solvent, opens the door to implanting the scaffolds freshly printed once lyophilized, while in a ductile state, and the hardening process to take place inside the body, as in the case of calcium phosphate cements. Second, even with a hydroxyapatite content of more than 92 wt.%, the flexural strength and toughness of the scaffolds after hardening are twice and five times those of the all -ceramic scaffolds obtained with the hydrogel-based inks, respectively. Statement of significance Overcoming the brittleness of ceramic scaffolds would extend the applicability of synthetic bone grafts to high load -bearing situations. In this work we developed a 3D printing ink by replacing the conventional hydrogel binder with a water -free polycaprolactone solution. The presence of polycaprolactone not only enhanced significantly the strength and toughness of the scaffolds while keeping the proportion of bioactive ceramic phase larger than 90 wt.%, but it also conferred flexibility and manipulability to the as -printed scaffolds. Since they are able to harden upon contact with water under physiological conditions, this opens up the possibility of implanting them immediately after printing, while they are still in a ductile state, with clear advantages for fixation and press -fit in the bone defect. (c) 2024 The Authors. Published by Elsevier Ltd on behalf of Acta Materialia Inc. This is an open access article under the CC BY license ( http://creativecommons.org/licenses/by/4.0/ )

JTD Keywords: 3-d printing, 3d printin, 3d printing, 3d-printing, Binders, Biocompatibility, Biomimetic hydroxyapatites, Biomimetics, Bone, Bone cement, Bone scaffolds, Brittleness, Calcium phosphate, Ceramic phase, Ceramic scaffolds, Ceramics, Ceramics particles, Fracture mechanics, Hardening, Hardening process, Hydrogels, Hydroxyapatite, Mechanical properties, Mechanical-properties, Plasticity, Polycaprolactone, Pyridine, Scaffolds, Scaffolds (biology), Self hardening, Strength and toughness, Thermodynamic properties, Viv

Different copolymers incorporating terpene oxide units (e.g., limonene oxide) have been evaluated considering thermal properties, degradability, and biocompatibility. Thus, polycarbonates and polyesters derived from aromatic, monocyclic and bicyclic anhydrides have been considered. Furthermore, ring substitution with myrcene terpene has been evaluated. All polymers were amorphous when evaluated directly from synthesis. However, spherulites could be observed after the slow evaporation of diluted chloroform solutions of polylimonene carbonate, with all isopropene units possessing an R configuration. This feature was surprising considering the reported information that suggested only the racemic polymer was able to crystallize. All polymers were thermally stable and showed a dependence of the maximum degradation rate temperature (from 242 °C to 342 °C) with the type of terpene oxide. The graduation of glass transition temperatures (from 44 °C to 172 °C) was also observed, being higher than those corresponding to the unsubstituted polymers. The chain stiffness of the studied polymers hindered both hydrolytic and enzymatic degradation while a higher rate was detected when an oxidative medium was assayed (e.g., weight losses around 12% after 21 days of exposure). All samples were biocompatible according to the adhesion and proliferation tests performed with fibroblast cells. Hydrophobic and mechanically consistent films (i.e., contact angles between 90° and 110°) were obtained after the evaporation of chloroform from the solutions, having different ratios of the studied biobased polyterpenes and poly(butylene succinate) (PBS). The blend films were comparable in tensile modulus and tensile strength with the pure PBS (e.g., values of 330 MPa and 7 MPa were determined for samples incorporating 30 wt.% of poly(PA-LO), the copolyester derived from limonene oxide and phthalic anhydride. Blends were degradable, biocompatible and appropriate to produce oriented-pore and random-pore scaffolds via a thermally-induced phase separation (TIPS) method and using 1,4-dioxane as solvent. The best results were attained with the blend composed of 70 wt.% PBS and 30 wt.% poly(PA-LO). In summary, the studied biobased terpene derivatives showed promising properties to be used in a blended form for biomedical applications such as scaffolds for tissue engineering.

JTD Keywords: alternating copolymerization, biobased materials, biodegradability, composites, crystallization, cyclohexene oxide, induced phase-separation, limonene oxide, mechanical-properties, polyesters, scaffolds, spherulites, terpene derivatives, thermal properties, thermally-induced phase separation, Acetone, Bio-based, Bio-based materials, Biobased materials, Biocompatibility, Biodegradability, Butenes, Cell culture, Chlorine compounds, Degradation, Evaporation, Glass transition, Limonene oxide, Monoterpenes, Phase separation, Poly (butylenes succinate), Polybutylene succinate, Property, Ring-opening copolymerization, Scaffolds, Spheru-lites, Tensile strength, Terpene derivatives, Thermal properties, Thermally induced phase separation, Thermally-induced phase separation, Thermally?induced phase separation, Thermodynamic properties, Thermogravimetric analysis

This work reports a simple and scalable strategy to prepare a series of thermoresponsive polyurethanes synthesized via copolymerization of dicyclohexyl diisocyanate with glycerol ethoxylate in a single one-pot system. These polyurethanes exhibit lower critical solution temperatures (LCST) at 57 degrees C. The LCST of synthesized polyurethane was determined from Dynamic Scanning Calorimetry and UV-vis measurements. Both the LCST and T-g of synthesized polyurethane was tuned by varying the ratio between hard segment (dicyclohexyl diisocyanate) and soft segment (glycerol ethoxylate). Thus, T-g values could be tuned from -54.6 degrees C to -19.9 degrees C for samples with different flexibility. The swelling and deswelling studies were done at room temperature and above the LCST respectively. The results showed that the swelling ratio increases with the increase of soft segment (glycerol ethoxylate) in synthesized polyurethanes. Furthermore, the mechanical properties of the membrane were studied by universal tensile testing measurements. Specifically, stress at break values varied from 0.35 +/- 0.07 MPa to 0.91 +/- 0.15 MPa for the tested membranes, whereas elongation at break data ranged from 101.9 +/- 20.9 % to 192.4 +/- 24.4 %, and Young's modulus varied from 0.35 +/- 0.03 MPa to 1.85 +/- 0.19 MPa. Tensile strength of the films increased with the increase of the hard segment and elongation at break decreased.

JTD Keywords: copolymerization, critical solution temperatures, polyurethanes, tensile strength, Biodegradable polyurethanes, Copolymerization, Critical solution temperatures, Glycol), Polymers, Polyurethanes, Solvent-free, Tensile strength, Thermoresponsive materials

Flexible electrochemical sensors based on electroactive materials have emerged as powerful analytical tools for biomedical applications requiring bioanalytes detection. Within this context, 3D printing is a remarkable technology for developing electrochemical devices, due to no design constraints, waste minimization, and batch manufacturing with high reproducibility. However, the fabrication of 3D printed electrodes is still limited by the in-house fabrication of conductive filaments, which requires the mixture of the electroactive material with melted of thermoplastic polymer (e.g., polylactic acid, PLA). Herein, a simple approach is presented for preparing electrochemical dopamine (DA) biosensors. Specifically, the surface of 3D-printed PLA specimens, which exhibit an elastic modulus and a tensile strength of 3.7 +/- 0.3 GPa and 47 +/- 1 MPa, respectively, is activated applying a 0.5 m NaOH solution for 30 min and, subsequently, poly(3,4-ethylenedioxythiophene) is polymerized in situ using aqueous solvent. The detection of DA with the produced sensors has been demonstrated by cyclic voltammetry, differential pulse voltammetry, and chronoamperometry. In summary, the obtained results reflect that low-cost electrochemical sensors, which are widely used in medicine and biotechnology, can be rapidly fabricated using the proposed approach that, although based on additive manufacturing, does not require the preparation of conductive filaments.

JTD Keywords: 3d printers, Additive manufacturing, Amines, Batch manufacturing, Biomedical applications, Chronoamperometry, Conducting polymer, Conducting polymers, Conductive filaments, Conservation, Cyclic voltammetry, Differential pulse voltammetry, Electroactive material, Electrochemical biosensor, Electrochemical devices, Electrochemical sensors, Electrodes, Electron emission, Flexible electrode, High reproducibility, Medical applications, Neurophysiology, Poly-3 ,4-ethylenedioxythiophene, Polyesters, Polylactic aci, Sodium hydroxide, Tensile strength, Thermoplastic polymer

Extracellular matrix (ECM) proteins are key mediators of cell/material interactions. The surface density and conformation of these proteins adsorbed on the material surface influence cell adhesion and the cellular response. We have previously shown that subtle variations in surface chemistry lead to drastic changes in the conformation of adsorbed fibronectin (FN). On poly(ethyl acrylate) (PEA), FN unfolds and displays domains for cell adhesion and FN-FN interaction, whereas on poly(methyl acrylate) (PMA) – with only one methyl group less – FN remains globular as it is in solution. The effect of the strength of the protein/material interaction in cell response, and its relation to protein density and conformation, has received limited attention so far. In this work, we used FN-functionalized AFM cantilevers to evaluate, via force spectroscopy, the strength of interaction between fibronectin and the underlying polymer which controls FN conformation (PEA and PMA). We found that the strength of FN/PEA interaction is significantly higher than FN/PMA, which limits the mobility of FN layer on PEA, reduces the ability of cells to mechanically reorganize FN and then leads to enhanced proteolysis and degradation of the surrounding matrix with compromised cell viability. By contrast, both PEA and PMA support cell adhesion when FN density is increased and also in the presence of serum or other serum proteins, including vitronectin (VN) and bovine serum albumin (BSA), which provide a higher degree of mobility to the matrix. Statement of Significance: The identification of parameters influencing cell response is of paramount importance for the design of biomaterials that will act as synthetic scaffolds for cells to anchor, grow and, eventually, become specialised tissues. Cells interact with materials through an intermediate layer of proteins adsorbed on the material surface. It is known that the density and conformation of these proteins determine cell behaviour. Here we show that the strength of protein/material interactions, which has received very limited attention so far, is key to understand the cellular response to biomaterials. Very strong protein/material interactions reduce the ability of cells to mechanically reorganize proteins at the material interface which results in enhanced matrix degradation, leading ultimately to compromised cell viability.

JTD Keywords: Fibronectin adsorption, Fibronectin remodeling, Protein mobility, Protein-material interaction strength

Summary: While in clinical settings, bone mineral density measured by computed tomography (CT) remains the key indicator for bone fracture risk, there is an ongoing quest for more engineering mechanics-based approaches for safety analyses of the skeleton. This calls for determination of suitable material properties from respective CT data, where the traditional approach consists of regression analyses between attenuation-related grey values and mechanical properties. We here present a physics-oriented approach, considering that elasticity and strength of bone tissue originate from the material microstructure and the mechanical properties of its elementary components. Firstly, we reconstruct the linear relation between the clinically accessible grey values making up a CT, and the X-ray attenuation coefficients quantifying the intensity losses from which the image is actually reconstructed. Therefore, we combine X-ray attenuation averaging at different length scales and over different tissues, with recently identified 'universal' composition characteristics of the latter. This gives access to both the normally non-disclosed X-ray energy employed in the CT-device and to in vivo patient-specific and location-specific bone composition variables, such as voxel-specific mass density, as well as collagen and mineral contents. The latter feed an experimentally validated multiscale elastoplastic model based on the hierarchical organization of bone. Corresponding elasticity maps across the organ enter a finite element simulation of a typical load case, and the resulting stress states are increased in a proportional fashion, so as to check the safety against ultimate material failure. In the young patient investigated, even normal physiological loading is probable to already imply plastic events associated with the hydrated mineral crystals in the bone ultrastructure, while the safety factor against failure is still as high as five.

JTD Keywords: Bone, Bone mass density, Continuum micromechanics, Elastoplasticity, Spine, Strength, X-ray physics