by Keyword: In-vitro degradation
Claudia, GM, Ivan, G, Laia, OM, Emilio, JP, Maria-Pau, G, Maurizio, V, Luis, CJ, Marta, P, (2023). Influence of ECAP process on mechanical, corrosion and bacterial properties of Zn-2Ag alloy for wound closure devices Materials & Design 228, 111817 
Actual polymeric wound closure devices are not optimal for load-bearing applications due to the low mechanical properties and the risk of inflammation and bacterial infection mainly produced by multifil-ament and braided configurations. Biodegradable metallic Zn alloys are promising materials candidates; however, mechanical performance, corrosion behaviour, and biological response should be controlled in order to inhibit the risk of inflammation and bacterial infection. To this end, a Zn-2Ag (2 wt% Ag) alloy was processed by ECAP to evaluate the concurrent combined effect of grain refinement and Ag alloying on biodegradation and antibacterial activity. Two ECAP cycles were successfully applied to a Zn-2Ag alloy obtaining a homogeneous ultra-fine-grained structure in which nanoindentation maps suggested isotro-pic mechanical properties. Lower UTS and YS with higher elongation was reported after ECAP with similar corrosion rates as before processing. ECAP processed samples showed a homogeneous Ag+ release below the minimum inhibitory concentration for S. Aureus and no antibacterial effect was observed by diffusion. As expected, the presence of Ag in Zn-Ag alloys reduced bacterial attachment. Nevertheless, ECAP processed Zn-2Ag provided an excellent antibacterial activity after 3 h probably caused by the uniformly degraded and thus, non- stable, surface observed after bacterial adhesion.(c) 2023 The Authors. Published by Elsevier Ltd. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).
JTD Keywords: Behavior, Binary alloys, Biodegradable zinc-alloys, Biomaterials, Equal channel angular pressing, Grain-refinement, In-vitro degradation, Mg, Microstructure, Nanoindentation, Progress, Staphylococcus-aureus, Temperature superplasticity, Ultrafine-grained materials, Zinc alloys, Zn alloys
Chausse, V, Iglesias, C, Bou-Petit, E, Ginebra, MP, Pegueroles, M, (2023). Chemical vs thermal accelerated hydrolytic degradation of 3D-printed PLLA/PLCL bioresorbable stents: Characterization and influence of sterilization Polymer Testing 117, 107817
Bioresorbable stents (BRS) are designed to provide initial sufficient mechanical support to prevent vessel recoil while being degraded until their complete resorption. Therefore, degradation rate of BRS plays a crucial role in successful stent performance. This work presents a complete study on the degradation of poly-llactic acid (PLLA) and poly(lactic-co-epsilon-caprolactone) (PLCL) stents fabricated by solvent-cast direct-writing (SC-DW) through two different accelerated assays: alkaline medium at 37 degrees C for 10 days and PBS at 50 degrees C for 4 months. On retrieval, degraded stents were characterized in terms of mass loss, molecular weight (Mw), thermal and mechanical properties. The results showed that under alkaline conditions, stents underwent surface erosion, whereas stents immersed in PBS at 50 degrees C experienced bulk degradation. M-n decrease was accurately described by the autocatalyzed kinetic model, with PLCL showing a degradation rate 1.5 times higher than PLLA. Additionally, stents were subjected to gamma-irradiation and ethylene oxide (EtO) sterilization. Whereas EtOsterilized stents remained structurally unaltered, gamma-irradiated stents presented severe deterioration as a result of extensive chain scission.
JTD Keywords: Acid, Behavior, Bioresorbable stents, Copolymer, Hydrolytic degradation, In-vitro degradation, Mechanical-properties, Molecular-weight, Poly(l-lactide), Poly-l-lactic acid, Poly-l-lactide, Scaffolds, Solvent-cast direct-writing, Sterilization