DONATE

Publications

by Keyword: Mechanical test

Serra, T., Navarro, M., Planell, J. A., (2012). Fabrication and characterization of biodegradable composite scaffolds for tissue engineering Innovative Developments in Virtual and Physical Prototyping 5th International Conference on Advanced Research and Rapid Prototyping (ed. Margarida, T., Ferreira, D.), Taylor & Francis (Leiria, Portugal) VR@P, 67-72

In this study, polylactic acid (PLA) and polyethylene glycol (PEG) were combined with soluble CaP glass particles and processed by rapid prototyping to obtain fully biodegradable structures for Tissue Engineering applications. The obtained 3D biodegradable structures were characterized in terms of their architecture and mechanical properties. The scaffold morphology, internal micro-architecture and mechanical properties were evaluated using Scanning Electron Microscopy (SEM), micro-computed tomography (micro-CT) and mechanical testing, respectively. Well defined structures with pore size of 350-400μm (in the axial view), struts width of approximately 70-80μm, and a porosity ranging between 60-65% were obtained. The combination RP and PLA/PEG/CaP glass turned into promising fully degradable, mechanically stable, bioactive and biocompatible composite scaffolds for TE.

JTD Keywords: Axial view, Biodegradable composites, Composite scaffolds, Glass particles, Mechanically stable, Micro architectures, Micro computed tomography (micro-CT), Poly lactic acid, Scaffold morphology, Tissue engineering applications, Well-defined structures, Bioactive glass, Mechanical properties, Mechanical testing, Polyethylene glycols, Polymer blends, Rapid prototyping, Scaffolds (biology), Scanning electron microscopy, Computerized tomography


Charles-Harris, M., del Valle, S., Hentges, E., Bleuet, P., Lacroix, D., Planell, J. A., (2007). Mechanical and structural characterisation of completely degradable polylactic acid/calcium phosphate glass scaffolds Biomaterials 28, (30), 4429-4438

This study involves the mechanical and structural characterisation of completely degradable scaffolds for tissue engineering applications. The scaffolds are a composite of polylactic acid (PLA) and a soluble calcium phosphate glass, and are thus completely degradable. A factorial experimental design was applied to optimise scaffold composition prior to simultaneous microtomography and micromechanical testing. Synchrotron X-ray microtomography combined with in situ micromechanical testing was performed to obtain three-dimensional 3D images of the scaffolds under compression. The 3D reconstruction was converted into a finite element mesh which was validated by simulating a compression test and comparing it with experimental results. The experimental design reveals that larger glass particle and pore sizes reduce the stiffness of the scaffolds, and that the porosity is largely unaffected by changes in pore sizes or glass weight content. The porosity ranges between 93% and 96.5%, and the stiffness ranges between 50 and 200 kPa. X-ray projections show a homogeneous distribution of the glass particles within the PLA matrix, and illustrate pore-wall breakage under strain. The 3D reconstructions are used qualitatively to visualise the distribution of the phases of the composite material, and to follow pore deformation under compression. Quantitatively, scaffold porosity, pore interconnectivity and surface/volume ratios have been calculated. Finite element analysis revealed the stress and strain distribution in the scaffold under compression, and could be used in the future to characterise the mechanical properties of the scaffolds.

JTD Keywords: Synchrotron x-ray microtomography, Mechanical test, Biodegradable, Glass, Scaffold, Finite element analysis