Publications

Biofabrication of three-dimensional (3D) cultures through the 3D Bioprinting technique opens new perspectives and applications of cell-laden hydrogels. However, to continue with the progress, new BioInks with specific properties must be carefully designed. In this study, we report the synthesis and 3D Bioprinting of an electroconductive BioInk made of gelatin/fibrinogen hydrogel, C2C12 mouse myoblast and 5% w/w of conductive poly (3,4-ethylenedioxythiophene) nanoparticles (PEDOT NPs). The influence of PEDOT NPs, incorporated in the cellladen BioInk, not only showed a positive effect in cells viability, differentiation and myotube functionalities, also allowed the printed constructs to behaved as BioCapacitors. Such devices were able to electrochemically store a significant amount of energy (0.5 mF/cm2), enough to self-stimulate as BioActuator, with typical contractions ranging from 27 to 38 mu N, during nearly 50 min. The biofabrication of 3D constructs with the proposed electroconductive BioInk could lead to new devices for tissue engineering, biohybrid robotics or bioelectronics.

JTD Keywords: 3d bioprinting, Animal, Animals, Bioactuator, Bioactuators, Biocapacitor, Biofabrication, Bioprinting, Biosensing techniques, C2c12 myoblasts, Cells, Chemistry, Electric conductivity, Electroconductive, Electroconductive bioink, Ethylenedioxythiophenes, Genetic procedures, Hydrogel, Hydrogels, Mice, Mouse, Pedot nps, Pedot nps,3d bioprinting,electroconductive bioink,bioactuator,biocapacito, Poly (3,4-ethylenedioxythiophene) nanoparticle, Printing, three-dimensional, Procedures, Skeletal-muscle,cytotoxicity,polymer, Synthesis (chemical), Three dimensional printing, Tissue engineering, Tissue scaffolds

Tissue engineering holds great promise for biomedical research and healthcare, offering alternatives to animal models and enabling tissue regeneration and organ transplantation. Three-dimensional (3D) bioprinting stands out for its design flexibility and reproducibility. Here, we present an integrated fluorescent light sheet bioprinting and imaging system that combines high printing speed (0.66 mm3 /s) and resolution (9 μm) with light sheet-based imaging. This approach employs direct laser patterning and a static light sheet for confined voxel crosslinking in photocrosslinkable materials. The developed bioprinter enables real-time monitoring of hydrogel crosslinking using fluorescent recovery after photobleaching (FRAP) and brightfield imaging as well as in situ light sheet imaging of cells. Human fibroblasts encapsulated in a thiol-ene click chemistry-based hydrogel exhibited high viability (83% ± 4.34%) and functionality. Furthermore, full-thickness skin constructs displayed characteristics of both epidermal and dermal layers and remained viable for 41 days. The integrated approach demonstrates the capabilities of light sheet bioprinting, offering high speed, resolution, and real-time characterization. Future enhancements involving solid-state laser scanning devices such as acousto-optic deflectors and modulators will further enhance resolution and speed, opening new opportunities in light-based bioprinting and advancing tissue engineering. This article is protected by copyright. All rights reserved.This article is protected by copyright. All rights reserved.

JTD Keywords: cadherin, collagen, culture, differentiation, fluorescence microscopy, full-thickness skin model, hydrogels, light sheet bioprinter, light sheet fluorescence microscopy, proliferation, survival, tissue engineering, Animal, Animals, Biofabrication, Bioprinting, Cell culture, Crosslinking, Fluorescence, Fluorescence microscopy, Full-thickness skin model, Hair follicle, Human, Humans, Hydrogel, Hydrogels, Image resolution, Laser patterning, Light sheet, Light sheet bioprinter, Light sheet fluorescence microscopy, Molecular biology, Photobleaching, Printing, three-dimensional, Procedures, Reproducibility, Reproducibility of results, Skin model, Three dimensional printing, Tissue, Tissue engineering, Tissue regeneration, Tissue scaffolds, Tissues engineerings

The functionalization of 3D-printed poly-l-lactic acid (PLLA) and poly(l-lactic-co-ε-caprolactone) (PLCL) bioresorbable stents has been successfully achieved with linear RGDS and YIGSR peptides, as well as a dual platform containing both motifs within a single biomolecule.

JTD Keywords: adsorbed fibrinogen, chemistry, endothelialization, immobilization, platelets, plla, selectivity, surface, titanium, Absorbable implants, Cell adhesion, Endothelial cells, In-vitro hemocompatibility, Peptides, Polymers, Printing, three-dimensional, Stents, Tyrosyl-isoleucyl-glycyl-seryl-arginine

Hydrothermal (H) processes accelerate the hydrolysis reaction of α-tricalcium phosphate (α-TCP) compared to the long-established biomimetic (B) treatments. They are of special interest for patient-specific 3D-printed bone graft substitutes, where the manufacturing time represents a critical constraint. Altering the reaction conditions has implications for the physicochemical properties of the reaction product. However, the impact of the changes produced by the hydrothermal reaction on the in vivo performance was hitherto unknown. The present study compares the bone regeneration potential of 3D-printed α-TCP scaffolds hardened using these two treatments in rabbit condyle monocortical defects. Although both consolidation processes resulted in biocompatible scaffolds with osseointegrative and osteoconductive properties, the amount of newly formed bone increased by one third in the hydrothermal vs the biomimetic samples. B and H scaffolds consisted mostly of high specific surface area calcium-deficient hydroxyapatite (38 and 27 m2 g-1, respectively), with H samples containing also 10 wt.% β-tricalcium phosphate (β-TCP). The shrinkage produced during the consolidation process was shown to be very small in both cases, below 3%, and smaller for H than for B samples. The differences in the in vivo performance were mainly attributed to the distinct crystallisation nanostructures, which proved to have a major impact on permeability and protein adsorption capacity, using BSA as a model protein, with B samples being highly impermeable. Given the crucial role that soluble proteins play in osteogenesis, this is proposed to be a relevant factor behind the distinct in vivo performances observed for the two materials. Statement of significance: The possibility to accelerate the consolidation of self-setting calcium phosphate inks through hydrothermal treatments has aroused great interest due to the associated advantages for the development of 3D-printed personalised bone scaffolds. Understanding the implications of this approach on the in vivo performance of the scaffolds is of paramount importance. This study compares, for the first time, this treatment to the long-established biomimetic setting strategy in terms of osteogenic potential in vivo in a rabbit model, and relates the results obtained to the physicochemical properties of the 3D-printed scaffolds (composition, crystallinity, nanostructure, nanoporosity) and their interaction with soluble proteins.

JTD Keywords: 3d printing, behavior, biomimetic, bone scaffolds, calcium phosphate, deficient hydroxyapatite, design, graft, hydrothermal, in vivo, morbidity, osteoinduction, porosity, standard, tricalcium phosphate, 3d printing, Animals, Biomimetic, Biomimetics, Bone regeneration, Bone scaffolds, Calcium phosphate, Calcium phosphates, Fibula free-flap, Humans, Hydrothermal, In vivo, Osteogenesis, Printing, three-dimensional, Rabbits, Tissue scaffolds

Porosity plays a key role on the osteogenic performance of bone scaffolds. Direct Ink Writing (DIW) allows the design of customized synthetic bone grafts with patient-specific architecture and controlled macroporosity. Being an extrusion-based technique, the scaffolds obtained are formed by arrays of cylindrical filaments, and therefore have convex surfaces. This may represent a serious limitation, as the role of surface curvature and more specifically the stimulating role of concave surfaces in osteoinduction and bone growth has been recently highlighted. Hence the need to design strategies that allow the introduction of concave pores in DIW scaffolds. In the current study, we propose to add gelatin microspheres as a sacrificial material in a self-setting calcium phosphate ink. Neither the phase transformation responsible for the hardening of the scaffold nor the formation of characteristic network of needle-like hydroxyapatite crystals was affected by the addition of gelatin microspheres. The partial dissolution of the gelatin resulted in the creation of spherical pores throughout the filaments and exposed on the surface, increasing filament porosity from 0.2 % to 67.9 %. Moreover, the presence of retained gelatin proved to have a significant effect on the mechanical properties, reducing the strength but simultaneously giving the scaffolds an elastic behavior, despite the high content of ceramic as a continuous phase. Notwithstanding the inherent difficulty of in vitro cultures with this highly reactive material an enhancement of MG-63 cell proliferation, as well as better spreading of hMSCs was recorded on the developed scaffolds. Statement of significance: Recent studies have stressed the role that concave surfaces play in tissue regeneration and, more specifically, in osteoinduction and osteogenesis. Direct ink writing enables the production of patient-specific bone grafts with controlled architecture. However, besides many advantages, it has the serious limitation that the surfaces obtained are convex. In this article, for the first time we develop a strategy to introduce concave pores in the printed filaments of biomimetic hydroxyapatite by incorporation and partial dissolution of gelatin microspheres. The retention of part of the gelatin results in a more elastic behavior compared to the brittleness of hydroxyapatite scaffolds, while the needle-shaped nanostructure of biomimetic hydroxyapatite is maintained and gelatin-coated concave pores on the surface of the filaments enhance cell spreading. © 2021 The Authors

JTD Keywords: 3d printing, bioceramics, biomimetic, bone, bone regeneration, concavity, concavity, bone regeneration, gelatin, hydrogel, hydroxyapatite, microspheres, osteoinduction, porosity, porous filament, substitutes, tissue-growth, 3d printing, Biomimetic, Biomimetics, Calcium-phosphate scaffolds, Concavity, bone regeneration, Durapatite, Gelatin, Humans, Hydroxyapatite, Porosity, Porous filament, Printing, three-dimensional, Tissue engineering, Tissue scaffolds