Pinera-Avellaneda, David, Buxadera-Palomero, Judit, Delint, Rosalia Cuahtecontzi, Dalby, Matthew J, Burgess, Karl V, Ginebra, Maria-Pau, Ruperez, Elisa, Manero, Jose Maria, (2024). Gallium and silver-doped titanium surfaces provide enhanced osteogenesis, reduce bone resorption and prevent bacterial infection in co-culture Acta Biomaterialia 180, 154-170

Bacterial infection remains a significant problem associated with orthopaedic surgeries leading to surgical site infection (SSI). This unmet medical need can become an even greater complication when surgery is due to malignant bone tumor. In the present study, we evaluated in vitro titanium (Ti) implants subjected to gallium (Ga) and silver (Ag)-doped thermochemical treatment as strategy to prevent SSI and improve osteointegration in bone defects caused by diseases such as osteoporosis, bone tumor, or bone metastasis. Firstly, as Ga has been reported to be an osteoinductive and anti-resorptive agent, its performance in the mixture was proved by studying human mesenchymal stem cells (hMSC) and pre-osteoclasts (RAW264.7) behaviour. Then, the antibacterial potential provided by Ag was assessed by resembling "The Race for the Surface" between hMSC and Pseudomonas aeruginosa in two co-culture methods. Moreover, the presence of quorum sensing molecules in the co-culture was evaluated. The results highlighted the suitability of the mixture to induce osteodifferentiation and reduce osteoclastogenesis in vitro . Furthermore, the GaAg surface promoted strong survival rate and retained osteoinduction potential of hMSCs even after bacterial inoculation. Therefore, GaAg-modified titanium may be an ideal candidate to repair bone defects caused by excessive bone resorption, in addition to preventing SSI.

JTD Keywords: Antibacteria, Antibacterial, Bone resorption, Expression, Gallium, In-vitro, Ligan, Nf-kappa-b, Nfatc1, Osteoclast formation, Phosphatase, Receptor activator, Silver, Ti metal, Titanium


Humbert, P, Kampleitner, C, De Lima, J, Brennan, MA, Lodoso-Torrecilla, I, Sadowska, JM, Blanchard, F, Canal, C, Ginebra, MP, Hoffmann, O, Layrolle, P, (2024). Phase composition of calcium phosphate materials affects bone formation by modulating osteoclastogenesis Acta Biomaterialia 176, 417-431

Human mesenchymal stromal cells (hMSCs) seeded on calcium phosphate (CaP) bioceramics are extensively explored in bone tissue engineering and have recently shown effective clinical outcomes. In previous pre-clinical studies, hMSCs-CaP-mediated bone formation was preceded by osteoclastogenesis at the implantation site. The current study evaluates to what extent phase composition of CaPs affects the osteoclast response and ultimately influence bone formation. To this end, four different CaP bioceramics were used, hydroxyapatite (HA), beta-tricalcium phosphate (beta-TCP) and two biphasic composites of HA/beta- TCP ratios of 60/40 and 20/80 respectively, for in vitro osteoclast differentiation and correlation with in vivo osteoclastogenesis and bone formation. All ceramics allowed osteoclast formation in vitro from mouse and human precursors, except for pure HA, which significantly impaired their maturation. Ectopic implantation alongside hMSCs in subcutis sites of nude mice revealed new bone formation at 8 weeks in all conditions with relative amounts for beta-TCP > biphasic CaPs > HA. Surprisingly, while hMSCs were essential for osteoinduction, their survival did not correlate with bone formation. By contrast, the degree of early osteoclastogenesis (2 weeks) seemed to define the extent of subsequent bone formation. Together, our findings suggest that the osteoclastic response could be used as a predictive marker in hMSC-CaPbased bone regeneration and strengthens the need to understand the underlying mechanisms for future biomaterial development. Statement of significance The combination of mesenchymal stromal cells (MSCs) and calcium phosphate (CaP) materials has demonstrated its safety and efficacy for bone regeneration in clinical trials, despite our insufficient understanding of the underlying biological mechanisms. Osteoclasts were previously suggested as key mediators between the early inflammatory phase following biomaterial implantation and the subsequent bone formation. Here we compared the affinity of osteoclasts for various CaP materials with different ratios of hydroxyapatite to beta-tricalcium phosphate. We found that osteoclast formation, both in vitro and at early stages in vivo, correlates with bone formation when the materials were implanted alongside MSCs in mice. Surprisingly, MSC survival did not correlate with bone formation, suggesting that the number or phenotype of osteoclasts formed was more important. (c) 2024 The Author(s). Published by Elsevier Ltd on behalf of Acta Materialia Inc. This is an open access article under the CC BY license ( http://creativecommons.org/licenses/by/4.0/ )

JTD Keywords: Acid phosphatase tartrate resistant isoenzyme, Animal, Animal cell, Animal experiment, Animal tissue, Animals, Article, Beta-tricalcium phosphate, Bioceramics, Biocompatible materials, Biomaterial, Bone, Bone development, Bone formation, Bone regeneration, Calcium phosphate, Calcium phosphate materials, Calcium phosphates, Cd14 antigen, Cell differentiation, Cell engineering, Cell maturation, Cell survival, Ceramics, Chemical composition, Controlled study, Correlation analysis, Correlation coefficient, Data correlation, Durapatite, Engraftment, Flowcharting, Human, Human cell, Human mesenchymal stromal cell, Human mesenchymal stromal cells, Humans, Hydroxyapatite, Hydroxyapatites, In vitro study, In vivo study, In-vitro, In-vivo, Mammals, Marrow stromal cells, Material composition, Material compositions, Mesenchymal stroma cell, Mesenchymal stromal cells, Mice, Mice, nude, Monocyte, Mouse, Nonhuman, Nude mouse, Ossification, Osteoclast, Osteoclastogenesis, Osteoclasts, Osteogenesis, Osteoinduction, Phase composition, Regeneration strategies, Resorption, Scaffolds, Stem-cells, Subcutaneous tissue, Tissue engineering, Transmission control protocol, Tri-calcium phosphates, Vimentin


Piñera-Avellaneda, D, Buxadera-Palomero, J, Ginebra, MP, Rupérez, E, Manero, JM, (2023). Gallium-doped thermochemically treated titanium reduces osteoclastogenesis and improves osteodifferentiation Frontiers In Bioengineering And Biotechnology 11, 1303313

Excessive bone resorption is one of the main causes of bone homeostasis alterations, resulting in an imbalance in the natural remodeling cycle. This imbalance can cause diseases such as osteoporosis, or it can be exacerbated in bone cancer processes. In such cases, there is an increased risk of fractures requiring a prosthesis. In the present study, a titanium implant subjected to gallium (Ga)-doped thermochemical treatment was evaluated as a strategy to reduce bone resorption and improve osteodifferentiation. The suitability of the material to reduce bone resorption was proven by inducing macrophages (RAW 264.7) to differentiate to osteoclasts on Ga-containing surfaces. In addition, the behavior of human mesenchymal stem cells (hMSCs) was studied in terms of cell adhesion, morphology, proliferation, and differentiation. The results proved that the Ga-containing calcium titanate layer is capable of inhibiting osteoclastogenesis, hypothetically by inducing ferroptosis. Furthermore, Ga-containing surfaces promote the differentiation of hMSCs into osteoblasts. Therefore, Ga-containing calcium titanate may be a promising strategy for patients with fractures resulting from an excessive bone resorption disease.Copyright © 2023 Piñera-Avellaneda, Buxadera-Palomero, Ginebra, Rupérez and Manero.

JTD Keywords: biology, bone metastasis, differentiation, ferroptosis, gallium, iron, mouse, osteoclast, osteoporosis, Bone metastasis, Ferroptosis, Gallium, Osteoclast, Osteoporosis, Ti metal, Titanium implant


Diez-Escudero, A., Torreggiani, E., Di Pompo, G., Espanol, M., Persson, C., Ciapetti, G., Baldini, N., Ginebra, M. P., (2019). Effect of calcium phosphate heparinization on the in vitro inflammatory response and osteoclastogenesis of human blood precursor cells Journal of Tissue Engineering and Regenerative Medicine 13, (7), 1217-1229

The immobilization of natural molecules on synthetic bone grafts stands as a strategy to enhance their biological interactions. During the early stages of healing, immune cells and osteoclasts (OC) modulate the inflammatory response and resorb the biomaterial, respectively. In this study, heparin, a naturally occurring molecule in the bone extracellular matrix, was covalently immobilized on biomimetic calcium‐deficient hydroxyapatite (CDHA). The effect of heparin‐functionalized CDHA on inflammation and osteoclastogenesis was investigated using primary human cells and compared with pristine CDHA and beta-tricalcium phosphate (β-TCP). Biomimetic substrates led to lower oxidative stresses by neutrophils and monocytes than sintered β-TCP, even though no further reduction was induced by the presence of heparin. In contrast, heparinized CDHA fostered osteoclastogenesis. Optical images of stained TRAP positive cells showed an earlier and higher presence of multinucleated cells, compatible with OC at 14 days, while pristine CDHA and β-TCP present OC at 21–28 days. Although no statistically significant differences were found in the OC activity, microscopy images evidenced early stages of degradation on heparinized CDHA, compatible with osteoclastic resorption. Overall, the results suggest that the functionalization with heparin fostered the formation and activity of OC, thus offering a promising strategy to integrate biomaterials in the bone remodelling cycle by increasing their OC-mediated resorption.

JTD Keywords: Biomaterial, Heparin, Hydroxyapatite, Inflammation, Osteoclastogenesis


Sadowska, Joanna M., Wei, Fei, Guo, Jia, Guillem-Marti, Jordi, Ginebra, Maria-Pau, Xiao, Yin, (2018). Effect of nano-structural properties of biomimetic hydroxyapatite on osteoimmunomodulation Biomaterials 181, 318-332

Immune cells are sensitive to the microstructural and textural properties of materials. Tuning the structural features of synthetic bone grafts could be a valuable strategy to regulate the specific response of the immune system, which in turn modulates the activity of bone cells. The aim of this study was to analyse the effect of the structural characteristics of biomimetic calcium deficient hydroxyapatite (CDHA) on the innate immune response of macrophages and the subsequent impact on osteogenesis and osteoclastogenesis. Murine RAW 264.7 cells were cultured, under standard and inflammatory conditions, on chemically identical CDHA substrates that varied in microstructure and porosity. The impact on osteogenesis was evaluated by incubating osteoblastic cells (SaOS-2) with RAW-CDHA conditioned extracts. The results showed that macrophages were sensitive to different textural and structural properties of CDHA. Under standard conditions, the impact of inflammatory cytokine production by RAW cells cultured on CDHA played a significant role in the degradation of substrates, suggesting the impact of resorptive behaviour of RAW cells on biomimetic surfaces. Osteoblast differentiation was stimulated by the conditioned media collected from RAW cells cultured on needle-like nanostructured CDHA. The results demonstrated that needle-like nanostructured CDHA was able to generate a favourable osteoimmune environment to regulate osteoblast differentiation and osteogenesis. Under inflammatory conditions, the incubation of RAW cells with less porous CDHA resulted in a decreased gene expression and release of pro-inflammatory cytokines.

JTD Keywords: Calcium phosphates, Biomimetic hydroxyapatite, Osteoimmunomodulation, Inflammation, Osteogenesis, Osteoclastogesis


Ciapetti, G., Di Pompo, G., Avnet, S., Martini, D., Diez-Escudero, A., Montufar, E. B., Ginebra, M. P., Baldini, N., (2017). Osteoclast differentiation from human blood precursors on biomimetic calcium-phosphate substrates Acta Biomaterialia 50, 102-113

The design of synthetic bone grafts to foster bone formation is a challenge in regenerative medicine. Understanding the interaction of bone substitutes with osteoclasts is essential, since osteoclasts not only drive a timely resorption of the biomaterial, but also trigger osteoblast activity. In this study, the adhesion and differentiation of human blood-derived osteoclast precursors (OCP) on two different micro-nanostructured biomimetic hydroxyapatite materials consisting in coarse (HA-C) and fine HA (HA-F) crystals, in comparison with sintered stoichiometric HA (sin-HA, reference material), were investigated. Osteoclasts were induced to differentiate by RANKL-containing supernatant using cell/substrate direct and indirect contact systems, and calcium (Ca++) and phosphorus (P5+) in culture medium were measured. We observed that OCP adhered to the experimental surfaces, and that osteoclast-like cells formed at a rate influenced by the micro- and nano-structure of HA, which also modulate extracellular Ca++. Qualitative differences were found between OCP on biomimetic HA-C and HA-F and their counterparts on plastic and sin-HA. On HA-C and HA-F cells shared typical features of mature osteoclasts, i.e. podosomes, multinuclearity, tartrate acid phosphatase (TRAP)-positive staining, and TRAP5b-enzyme release. However, cells were less in number compared to those on plastic or on sin-HA, and they did not express some specific osteoclast markers. In conclusion, blood-derived OCP are able to attach to biomimetic and sintered HA substrates, but their subsequent fusion and resorptive activity are hampered by surface micro-nano-structure. Indirect cultures suggest that fusion of OCP is sensitive to topography and to extracellular calcium. Statement of Significance: The novelty of the paper is the differentiation of human blood-derived osteoclast precursors, instead of mouse-derived macrophages as used in most studies, directly on biomimetic micro-nano structured HA-based surfaces, as triggered by osteoblast-produced factors (RANKL/OPG), and influenced by chemistry and topography of the substrate(s). Biomimetic HA-surfaces, like those obtained in calcium phosphate cements, are very different from the conventional calcium phosphate ceramics, both in terms of topography and ion exchange. The role of these factors in modulating precursors’ differentiation and activity is analysed. The system is closely reproducing the physiological process of attachment of host cells and further maturation to osteoclasts toward resorption of the substrate, which occurs in vivo after filling bone defects with the calcium phosphate grafts.

JTD Keywords: Bone resorption, Differentiation, Hydroxyapatite, Ionic exchange, Osteoclasts, Topography


Diez-Escudero, A., Espanol, M., Montufar, E. B., Di Pompo, G., Ciapetti, G., Baldini, N., Ginebra, M. P., (2017). Focus ion beam/scanning electron microscopy characterization of osteoclastic resorption of calcium phosphate substrates Tissue Engineering Part C: Methods , 23, (2), 118-124

This article presents the application of dual focused ion beam/scanning electron microscopy (FIB-SEM) imaging for preclinical testing of calcium phosphates with osteoclast precursor cells and how this high-resolution imaging technique is able to reveal microstructural changes at a level of detail previously not possible. Calcium phosphate substrates, having similar compositions but different microstructures, were produced using low-and high-Temperature processes (biomimetic calcium-deficient hydroxyapatite [CDHA] and stoichiometric sintered hydroxyapatite, respectively). Human osteoclast precursor cells were cultured for 21 days before evaluating their resorptive potential on varying microstructural features. Alternative to classical morphological evaluation of osteoclasts (OC), FIB-SEM was used to observe the subjacent microstructure by transversally sectioning cells and observing both the cells and the substrates. Resorption pits, indicating OC activity, were visible on the smoother surface of high-Temperature sintered hydroxyapatite. FIB-SEM analysis revealed signs of acidic degradation on the grain surface under the cells, as well as intergranular dissolution. No resorption pits were evident on the surface of the rough CDHA substrates. However, whereas no degradation was detected by FIB sections in the material underlying some of the cells, early stages of OC-mediated acidic degradation were observed under cells with more spread morphology. Collectively, these results highlight the potential of FIB to evaluate the resorptive activity of OC, even in rough, irregular, or coarse surfaces where degradation pits are otherwise difficult to visualize.

JTD Keywords: Bone Regeneration, Calcium Phosphate, Focus Ion Beam, Osteoclast, Resorption, Scanning Electron Microscopy