Publications

Over the last decade, 3D-printed porous calcium phosphates have emerged in the market for customized bone reconstruction. However, despite their excellent biological properties, the inherent brittleness is an obstacle that limits their clinical applications, as the scaffolds must withstand the surgical procedures and the mechanical stresses once implanted. Low-temperature self-hardening calcium phosphate inks offer unique possibilities to be reinforced with polymers, as they do not require high-temperature treatments. This study compares two routes for incorporating poly (lactic-co-glycolic acid) (PLGA) into 3D-printed calcium phosphate scaffolds: i) the use of a PLGA solution as a binder in an alpha-tricalcium phosphate self-hardening ink; ii) the infiltration of a PLGA solution into previously hardened 3D-printed calcium-deficient hydroxyapatite scaffolds. The influence of the added PLGA on the physical-chemical properties, mechanical performance and in vitro biological properties is assessed using a commercially available biomimetic calcium phosphate scaffold as a control. The addition of PLGA increases the plastic deformation capacity and the strength, both in compression and bending, and significantly improves the work of fracture of the scaffolds, up to an 8-fold in compression when PLGA is incorporated as a binder in the ink. Moreover, screwability tests demonstrate the enhanced fixability of the composite scaffolds in a knife-edge ridge indication with challenging fixation in the jaw. Importantly, the improvement of the mechanical properties by the addition of PLGA does not impair the good cytocompatibility of the material. Regarding the two routes studied, the PLGA incorporation in the ink is the best option in terms of overall improvement of the mechanical performance and osteogenic cell response.

JTD Keywords: Alkaline-phosphatase, B. composites, C. mechanical properties, Composite scaffold, D. apatite, Differentiation, E. biomedical application, In-vivo, Join, Regeneration

One of humanity's greatest challenges is space exploration, which requires an in-depth analysis of the data continuously collected as a necessary input to fill technological gaps and move forward in several research sectors. Focusing on space crew healthcare, a critical issue to be addressed is tissue regeneration in extreme conditions. In general, it represents one of the hottest and most compelling goals of the scientific community and the development of suitable therapeutic strategies for the space environment is an urgent need for the safe planning of future long-term manned space missions. Osteopenia is a commonly diagnosed disease in astronauts due to the physiological adaptation to altered gravity conditions. In order to find specific solutions to bone damage in a reduced gravity environment, bone tissue engineering is gaining a growing interest. With the aim to critically investigate this topic, the here presented review reports and discusses bone tissue engineering scenarios in microgravity, from scaffolding to bioreactors. The literature analysis allowed to underline several key points, such as the need for (i) biomimetic composite scaffolds to better mimic the natural microarchitecture of bone tissue, (ii) uniform simulated microgravity levels for standardized experimental protocols to expose biological materials to the same testing conditions, and (iii) improved access to real microgravity for scientific research projects, supported by the so-called democratization of space.© 2022. The Author(s).

JTD Keywords: biomaterials, collagen/hydroxyapatite, composite scaffolds, in-vitro, mineralization, proliferation, regenerative medicine, stem-cells, vivo, Hydroxyapatite scaffolds

© BME-PT. Ultrasound micromolding (USM) preparation of hybrid scaffolds based on polylactide (PLA) and hydroxyapatite (HAp) particles has been evaluated. PLA was stable under the applied ultrasound source since a minimum degradation was detected. Porous materials were achieved using polyethylene glycol (PEG) and NaCl salts to the initial PLA and the subsequent leaching of the micromolded specimens. To avoid cavitation and decomposition problems during micromolding, it was necessary to use HAp free of typical synthesis impurities like carbonate and nitrate compounds. Compact PLA/HAp pieces allowed a maximum HAp load of 60 wt%, while porous specimens could be obtained with a maximum load of 38 wt%. Physical characterization of new scaffolds was performed by X-ray diffraction, spectroscopic and calorimetric techniques, stress-strain tests and contact angle measurements. Results indicated that a degree of porosity of 35% and relatively good mechanical properties could be achieved (i.e., 580 MPa, 4%, and 15.6 MPa for the Young modulus, elongation at break, and tensile strength, respectively). Scaffolds showed the positive effect of HAp and porosity on cell proliferation; this latter was 40% higher than that detected for non-porous PLA specimens.

JTD Keywords: apatite, conformation, fabrication, hydroxyapatite, micropieces, polymers, porous scaffolds, proliferation, tissue, ultrasound micromolding, vibration, Composite scaffolds, Hydroxyapatite, Micropieces, Porous scaffolds, Processing technologies, Ultrasound micromolding

Bioactive nanocomposite scaffolds with cell-adhesive surface have excellent bone regeneration capacities. Fibronectin (FN)-immobilized nanobioactive glass (nBG)/polycaprolactone (PCL) (FN-nBG/PCL) scaffolds with an open pore architecture were generated by a robotic-dispensing technique. The surface immobilization level of FN was significantly higher on the nBG/PCL scaffolds than on the PCL scaffolds, mainly due to the incorporated nBG that provided hydrophilic chemical-linking sites. FN-nBG/PCL scaffolds significantly improved cell responses, including initial anchorage and subsequent cell proliferation. Although further in-depth studies on cell differentiation and the in vivo animal responses are required, bioactive nanocomposite scaffolds with cell-favoring surface are considered to provide promising three-dimensional substrate for bone regeneration.

JTD Keywords: Bone scaffolds, Cell response, Fibronectin, Nanobioactive glass, Nanocomposites, Polycaprolactone, Bone, Cell proliferation, Cells, Cytology, Glass, Nanocomposites, Polycaprolactone, Robotics, Bone scaffolds, Bone tissue engineering, Cell response, Fibronectin, Fibronectin immobilizations, Nano bioactive glass, Nanocomposite scaffolds, Three-dimensional substrates, Scaffolds (biology)

In this study, polylactic acid (PLA) and polyethylene glycol (PEG) were combined with soluble CaP glass particles and processed by rapid prototyping to obtain fully biodegradable structures for Tissue Engineering applications. The obtained 3D biodegradable structures were characterized in terms of their architecture and mechanical properties. The scaffold morphology, internal micro-architecture and mechanical properties were evaluated using Scanning Electron Microscopy (SEM), micro-computed tomography (micro-CT) and mechanical testing, respectively. Well defined structures with pore size of 350-400μm (in the axial view), struts width of approximately 70-80μm, and a porosity ranging between 60-65% were obtained. The combination RP and PLA/PEG/CaP glass turned into promising fully degradable, mechanically stable, bioactive and biocompatible composite scaffolds for TE.

JTD Keywords: Axial view, Biodegradable composites, Composite scaffolds, Glass particles, Mechanically stable, Micro architectures, Micro computed tomography (micro-CT), Poly lactic acid, Scaffold morphology, Tissue engineering applications, Well-defined structures, Bioactive glass, Mechanical properties, Mechanical testing, Polyethylene glycols, Polymer blends, Rapid prototyping, Scaffolds (biology), Scanning electron microscopy, Computerized tomography