by Keyword: Polyurethanes

Fontana-Escartín, A, Lanzalaco, S, Zhilev, G, Armelin, E, Bertran, O, Alemán, C, (2024). Oxygen plasma treated thermoplastics as integrated electroresponsive sensors Materials Today Communications 38, 107653

Polypropylene (PP), thermoplastic polyurethane (TPU), polyethylene terephthalate glycol (PETG) and polylactic acid (PLA) 3D printed specimens, which are intrinsically non-electroresponsive materials, have been converted into electroresponsive electrodes applying a low-pressure oxygen plasma treatment. After complete chemical, morphological and electrochemical characterization, plasma treated samples have been applied as integrated electrochemical sensors for detecting dopamine and serotonin by cyclic voltammetry and chronoamperometry. Results show differences in the sensing behavior, which have been explained on the basis of the chemical structure of the pristine materials. While plasma treated PLA exhibits the highest performance as electrochemical sensor in terms of sensitivity (lowest limits of detection and quantification) and selectivity (against uric acid and ascorbic acid as interfering substances), plasma treated PP displays the poorest behavior due to its low polarity compared to PLA 3D-printed electrodes. Instead, plasma treated TPU and PETG shows a very good response, much closer to PLA, as sensitive electrodes towards neurotransmitter molecules (dopamine and serotonin). Overall, results open a new door for the fabrication of electrochemical conductive sensors using intrinsically insulating materials, without the need of chemical functionalization processes.

JTD Keywords: 3d printing, Amines, Ascorbic acid, Chemical characterization, Cyclic voltammetry, Dopamine, Electrochemical characterizations, Electrochemical sensor s, Electrochemical sensors, Electrode materials, Electroresponsive materials, Low-pressure oxygen-plasma treatments, Morphological characterization, Multiwalled carbon nanotubes (mwcn), Neurophysiology, Oxygen, Oxygen plasmas, Plastic bottles, Polyethylene terephthalate glycol, Polyethylene terephthalate glycols, Polyethylene terephthalates, Polylact i c acid, Polylactic acid, Polylactic acid pla, Polyols, Polypropylene, Polypropylene oxides, Polypropylenes, Polyurethanes, Reinforced plastics, Supercapacitors, Thermoplast i c polyurethane, Thermoplastic polyurethane, Thermoplastic polyurethanes

Maiti, B, Nandi, M, Bonardd, S, Franco, L, Puiggali, J, Enshaei, H, Aleman, C, Diaz, DD, (2021). Efficient One-Pot Preparation of Thermoresponsive Polyurethanes with Lower Critical Solution Temperatures Chempluschem 86, 1570-1576

This work reports a simple and scalable strategy to prepare a series of thermoresponsive polyurethanes synthesized via copolymerization of dicyclohexyl diisocyanate with glycerol ethoxylate in a single one-pot system. These polyurethanes exhibit lower critical solution temperatures (LCST) at 57 degrees C. The LCST of synthesized polyurethane was determined from Dynamic Scanning Calorimetry and UV-vis measurements. Both the LCST and T-g of synthesized polyurethane was tuned by varying the ratio between hard segment (dicyclohexyl diisocyanate) and soft segment (glycerol ethoxylate). Thus, T-g values could be tuned from -54.6 degrees C to -19.9 degrees C for samples with different flexibility. The swelling and deswelling studies were done at room temperature and above the LCST respectively. The results showed that the swelling ratio increases with the increase of soft segment (glycerol ethoxylate) in synthesized polyurethanes. Furthermore, the mechanical properties of the membrane were studied by universal tensile testing measurements. Specifically, stress at break values varied from 0.35 +/- 0.07 MPa to 0.91 +/- 0.15 MPa for the tested membranes, whereas elongation at break data ranged from 101.9 +/- 20.9 % to 192.4 +/- 24.4 %, and Young's modulus varied from 0.35 +/- 0.03 MPa to 1.85 +/- 0.19 MPa. Tensile strength of the films increased with the increase of the hard segment and elongation at break decreased.

JTD Keywords: copolymerization, critical solution temperatures, polyurethanes, tensile strength, Biodegradable polyurethanes, Copolymerization, Critical solution temperatures, Glycol), Polymers, Polyurethanes, Solvent-free, Tensile strength, Thermoresponsive materials