del-Mazo-Barbara, Laura, Ginebra, Maria-Pau, (2024). Self-hardening polycaprolactone/calcium phosphate inks for 3D printing of bone scaffolds: rheology, mechanical properties and shelf-life Materials & Design 243, 113035

The development of 3D-printed calcium phosphate bone grafts represents a breakthrough for personalized bone tissue engineering. However, their high brittleness is a limiting factor for clinical applications. The present work aims to overcome this drawback by developing a composite ink for direct ink writing using a polycaprolactone solution (20 wt% in pyridine) as binder for a self-hardening alpha-tricalcium phosphate powder. The ink consolidation results from a two-step process. First, evaporation of the solvent gives rise to a flexible green body, in which the polymer matrix retains the loose ceramic particles. Subsequently, upon contact with water, the hydrolysis of these particles creates a continuous network of biomimetic hydroxyapatite nanocrystals, with the consequent hardening of the ink. The presence of the polymer improves the mechanical properties, increasing the flexural strength from 2 to 4 MPa and the strain energy density from 0.2 to 1.1 kJ/m3. Unlike the inks based on hydrogel binders, where the hardening reaction starts as soon as the liquid and solid components are mixed, the ink prepared with the non-aqueous binder is stable, with over 5 months shelf life, and allows the hardening reaction to be triggered at will by contact with water.

JTD Keywords: 3d printing, Bone scaffold, Calcium phosphates, Mechanical propertie, Polycaprolactone


del-Mazo-Barbara, Laura, Johansson, Linh, Tampieri, Francesco, Ginebra, Maria-Pau, (2024). Toughening 3D printed biomimetic hydroxyapatite scaffolds: Polycaprolactone-based self-hardening inks Acta Biomaterialia 177, 506-524

The application of 3D printing to calcium phosphates has opened unprecedented possibilities for the fabrication of personalized bone grafts. However, their biocompatibility and bioactivity are counterbalanced by their high brittleness. In this work we aim at overcoming this problem by developing a self -hardening ink containing reactive ceramic particles in a polycaprolactone solution instead of the traditional approach that use hydrogels as binders. The presence of polycaprolactone preserved the printability of the ink and was compatible with the hydrolysis -based hardening process, despite the absence of water in the ink and its hydrophobicity. The microstructure evolved from a continuous polymeric phase with loose ceramic particles to a continuous network of hydroxyapatite nanocrystals intertwined with the polymer, in a configuration radically different from the polymer/ceramic composites obtained by fused deposition modelling. This resulted in the evolution from a ductile behavior, dominated by the polymer, to a stiffer behavior as the ceramic phase reacted. The polycaprolactone binder provides two highly relevant benefits compared to hydrogel-based inks. First, the handleability and elasticity of the as -printed scaffolds, together with the proven possibility of eliminating the solvent, opens the door to implanting the scaffolds freshly printed once lyophilized, while in a ductile state, and the hardening process to take place inside the body, as in the case of calcium phosphate cements. Second, even with a hydroxyapatite content of more than 92 wt.%, the flexural strength and toughness of the scaffolds after hardening are twice and five times those of the all -ceramic scaffolds obtained with the hydrogel-based inks, respectively. Statement of significance Overcoming the brittleness of ceramic scaffolds would extend the applicability of synthetic bone grafts to high load -bearing situations. In this work we developed a 3D printing ink by replacing the conventional hydrogel binder with a water -free polycaprolactone solution. The presence of polycaprolactone not only enhanced significantly the strength and toughness of the scaffolds while keeping the proportion of bioactive ceramic phase larger than 90 wt.%, but it also conferred flexibility and manipulability to the as -printed scaffolds. Since they are able to harden upon contact with water under physiological conditions, this opens up the possibility of implanting them immediately after printing, while they are still in a ductile state, with clear advantages for fixation and press -fit in the bone defect. (c) 2024 The Authors. Published by Elsevier Ltd on behalf of Acta Materialia Inc. This is an open access article under the CC BY license ( http://creativecommons.org/licenses/by/4.0/ )

JTD Keywords: 3-d printing, 3d printin, 3d printing, 3d-printing, Binders, Biocompatibility, Biomimetic hydroxyapatites, Biomimetics, Bone, Bone cement, Bone scaffolds, Brittleness, Calcium phosphate, Ceramic phase, Ceramic scaffolds, Ceramics, Ceramics particles, Fracture mechanics, Hardening, Hardening process, Hydrogels, Hydroxyapatite, Mechanical properties, Mechanical-properties, Plasticity, Polycaprolactone, Pyridine, Scaffolds, Scaffolds (biology), Self hardening, Strength and toughness, Thermodynamic properties, Viv


García-Mintegui, C, Chausse, V, Labay, C, Mas-Moruno, C, Ginebra, MP, Cortina, JL, Pegueroles, M, (2024). Dual peptide functionalization of Zn alloys to enhance endothelialization for cardiovascular applications Applied Surface Science 645, 158900

A new generation of fully bioresorbable metallic Zn-based alloys could be used for stenting applications; however, the initial surface degradation delays stent re-endothelialization. Thus, this work proposes a dual strategy to control the corrosion and accelerate the endothelialization of ZnMg and ZnAg biodegradable alloys. First, a stable polycaprolactone (PCL) coating is obtained and followed by its functionalization with either linear RGD (Arg-Gly-Asp) or REDV (Arg-Glu-Asp-Val) peptides or a dual peptide-based platform combining both sequences (RGD-REDV). Scratching tests showed neither delamination nor detachment of the polymeric coating. Potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS) measurements confirmed the corrosion resistance after PCL coating by revealing lower current density and higher absolute impedance values. X-ray photoelectron spectroscopy (XPS) and fluorescent microscopy confirmed the correct peptide immobilization onto PCL coated Zn alloys. The functionalized samples exhibited enhanced human umbilical vein endothelial cells (HUVEC) adhesion. The higher number of adhered cells to the functionalized surfaces with the RGD-REDV platform demonstrates the synergistic effect of combining both RGD and REDV sequences. Higher corrosion resistance together with enhanced endothelialization indicates that the dual functionalization of Zn alloys with PCL and peptide-based RGD-REDV platform holds great potential to overcome the clinical limitations of current biodegradable metal stents.

JTD Keywords: Binary alloys, Biodegradable metals, Bioresorbable, Cardiovascular applications, Cell adhesive peptides, Corrosion, Corrosion resistance, Corrosion resistant alloys, Corrosion resistant coatings, Degradation, Dual peptide-based platform, Electrochemical corrosion, Electrochemical impedance spectroscopy, Endothelial cells, Endothelialization, Functionalization, Functionalizations, In-vitro, Magnesium alloys, Metallics, Mg alloy, Peptides, Polycaprolactone coating, Polymer-coatings, Rgd-functionalization, Silver alloys, Stents, Surface, X ray photoelectron spectroscopy, Zinc, Zinc alloys, Zn alloys, Zn-based alloys


Barbosa, F, Garrudo, FFF, Alberte, PS, Resina, L, Carvalho, MS, Jain, A, Marques, AC, Estrany, F, Rawson, FJ, Aléman, C, Ferreira, FC, Silva, JC, (2023). Hydroxyapatite-filled osteoinductive and piezoelectric nanofibers for bone tissue engineering Science And Technology Of Advanced Materials 24, 2242242

Osteoporotic-related fractures are among the leading causes of chronic disease morbidity in Europe and in the US. While a significant percentage of fractures can be repaired naturally, in delayed-union and non-union fractures surgical intervention is necessary for proper bone regeneration. Given the current lack of optimized clinical techniques to adequately address this issue, bone tissue engineering (BTE) strategies focusing on the development of scaffolds for temporarily replacing damaged bone and supporting its regeneration process have been gaining interest. The piezoelectric properties of bone, which have an important role in tissue homeostasis and regeneration, have been frequently neglected in the design of BTE scaffolds. Therefore, in this study, we developed novel hydroxyapatite (HAp)-filled osteoinductive and piezoelectric poly(vinylidene fluoride-co-tetrafluoroethylene) (PVDF-TrFE) nanofibers via electrospinning capable of replicating the tissue's fibrous extracellular matrix (ECM) composition and native piezoelectric properties. The developed PVDF-TrFE/HAp nanofibers had biomimetic collagen fibril-like diameters, as well as enhanced piezoelectric and surface properties, which translated into a better capacity to assist the mineralization process and cell proliferation. The biological cues provided by the HAp nanoparticles enhanced the osteogenic differentiation of seeded human mesenchymal stem/stromal cells (MSCs) as observed by the increased ALP activity, cell-secreted calcium deposition and osteogenic gene expression levels observed for the HAp-containing fibers. Overall, our findings describe the potential of combining PVDF-TrFE and HAp for developing electroactive and osteoinductive nanofibers capable of supporting bone tissue regeneration.© 2023 The Author(s). Published by National Institute for Materials Science in partnership with Taylor & Francis Group.

JTD Keywords: composites, electrospinning, hydroxyapatite, piezoelectricity, promote, pvdf, pvdf-trfe, removal, scaffolds, temperature, Bone tissue engineering, Electrospinning, Electrospun polycaprolactone, Hydroxyapatite, Piezoelectricity, Pvdf-trfe


Molina, BG, Ocón, G, Silva, FM, Iribarren, JI, Armelin, E, Alemán, C, (2023). Thermally-induced shape memory behavior of polylactic acid/ polycaprolactone blends European Polymer Journal 196, 112230

A study of the shape memory effect on extruded polylactic acid (PLA) and polycaprolactone (PCL) blends, which were transformed into films and movable components of articulated specimens by hot pressing and 3D printing, respectively, is presented. After characterizing their chemical structure by FTIR spectroscopy and their wetta-bility, the thermal properties and mechanical response of the blends were evaluated and compared with those of neat PLA and PCL. The blends exhibited very good interfacial adhesion between the phases, even though they are immiscible polymers. The thermoresponsive shape memory effects of neat PLA, neat PCL and PLA/PCL blends with different compositions (90/30, 70/30 and 50/50 w/w%) were evaluated considering three consecutive heating-cooling cycles. Comparison of the initial permanent state geometry with the geometries achieved after each heating-cooling cycle for both films and 3D printed specimens, evidenced that the 70/30 w/w% blend exhibited the best behavior. Thus, the blends obtained with such composition showed the maximum reversibility between the temporary and permanent states (i.e. highest shape recovery capability) and shape fixing of such two states.

JTD Keywords: 3d printing, Fibers, Films, Poly(lactic acid), Polycaprolactone, Polylactic acid, Polymer, Shape fixing, Shape-memory polymers, Unimolecular micelles


Rubí-Sans, G., Recha-Sancho, L., Pérez-Amodio, S., Mateos-Timoneda, M. Á., Semino, C. E., Engel, E., (2020). Development of a three-dimensional bioengineered platform for articular cartilage regeneration Biomolecules 10, (1), 52

Degenerative cartilage pathologies are nowadays a major problem for the world population. Factors such as age, genetics or obesity can predispose people to suffer from articular cartilage degeneration, which involves severe pain, loss of mobility and consequently, a loss of quality of life. Current strategies in medicine are focused on the partial or total replacement of affected joints, physiotherapy and analgesics that do not address the underlying pathology. In an attempt to find an alternative therapy to restore or repair articular cartilage functions, the use of bioengineered tissues is proposed. In this study we present a three-dimensional (3D) bioengineered platform combining a 3D printed polycaprolactone (PCL) macrostructure with RAD16-I, a soft nanofibrous self-assembling peptide, as a suitable microenvironment for human mesenchymal stem cells’ (hMSC) proliferation and differentiation into chondrocytes. This 3D bioengineered platform allows for long-term hMSC culture resulting in chondrogenic differentiation and has mechanical properties resembling native articular cartilage. These promising results suggest that this approach could be potentially used in articular cartilage repair and regeneration.

JTD Keywords: 3D printing, Chondrogenic differentiation, Polycaprolactone, RAD16-I self-assembling peptide


Won, J. E., Mateos-Timoneda, M. A., Castaño, O., Planell, J. A., Seo, S. J., Lee, E. J., Han, C. M., Kim, H. W., (2015). Fibronectin immobilization on to robotic-dispensed nanobioactive glass/polycaprolactone scaffolds for bone tissue engineering Biotechnology Letters , 37, (4), 935-342

Bioactive nanocomposite scaffolds with cell-adhesive surface have excellent bone regeneration capacities. Fibronectin (FN)-immobilized nanobioactive glass (nBG)/polycaprolactone (PCL) (FN-nBG/PCL) scaffolds with an open pore architecture were generated by a robotic-dispensing technique. The surface immobilization level of FN was significantly higher on the nBG/PCL scaffolds than on the PCL scaffolds, mainly due to the incorporated nBG that provided hydrophilic chemical-linking sites. FN-nBG/PCL scaffolds significantly improved cell responses, including initial anchorage and subsequent cell proliferation. Although further in-depth studies on cell differentiation and the in vivo animal responses are required, bioactive nanocomposite scaffolds with cell-favoring surface are considered to provide promising three-dimensional substrate for bone regeneration.

JTD Keywords: Bone scaffolds, Cell response, Fibronectin, Nanobioactive glass, Nanocomposites, Polycaprolactone, Bone, Cell proliferation, Cells, Cytology, Glass, Nanocomposites, Polycaprolactone, Robotics, Bone scaffolds, Bone tissue engineering, Cell response, Fibronectin, Fibronectin immobilizations, Nano bioactive glass, Nanocomposite scaffolds, Three-dimensional substrates, Scaffolds (biology)


Rajzer, I., Menaszek, E., Kwiatkowski, R., Planell, J. A., Castaño, O., (2014). Electrospun gelatin/poly(ε-caprolactone) fibrous scaffold modified with calcium phosphate for bone tissue engineering Materials Science and Engineering: C 44, 183-190

In this study gelatin (Gel) modified with calcium phosphate nanoparticles (SG5) and polycaprolactone (PCL) were used to prepare a 3D bi-layer scaffold by collecting electrospun PCL and gelatin/SG5 fibers separately in the same collector. The objective of this study was to combine the desired properties of PCL and Gel/SG5 in the same scaffold in order to enhance mineralization, thus improving the ability of the scaffold to bond to the bone tissue. The scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR) and the wide angle X-ray diffraction (WAXD) measurements confirmed that SG5 nanoparticles were successfully incorporated into the fibrous gelatin matrix. The composite Gel/SG5/PCL scaffold exhibited more enhanced mechanical properties than individual Gel and Gel/SG5 scaffolds. The presence of SG5 nanoparticles accelerated the nucleation and growth of apatite crystals on the surface of the composite Gel/SG5/PCL scaffold in simulated body fluid (SBF). The osteoblast response in vitro to developed electrospun scaffolds (PCL and Gel/SG5/PCL) was investigated by using normal human primary NHOst cell lines. NHOst cell culture studies showed that higher alkaline phosphatase (ALP) activity and better mineralization were obtained in the case of composite materials than in pure PCL scaffolds. The mechanically strong PCL scaffold served as a skeleton, while the Gel/SG5 fibers facilitated cell spreading and mineralization of the scaffold.

JTD Keywords: Bilayer fibrous scaffold, Ceramic nanoparticles, Electrospinning, Gelatin, Polycaprolactone, Biomechanics, Bone, Calcium phosphate, Cell culture, Electrospinning, Fourier transform infrared spectroscopy, Mechanical properties, Mineralogy, Nanoparticles, Phosphatases, Polycaprolactone, Scanning electron microscopy, X ray diffraction, Polycaprolactone, Alkaline phosphatase activity, Bone tissue engineering, Calcium phosphate nanoparticles, Ceramic nanoparticles, Fibrous scaffolds, Gelatin, Simulated body fluids, Wide-angle x-ray diffraction, Electrospuns, Scaffolds (biology), Electrospinning