Publications

Laser surface micropatterning of dental-grade zirconia (3Y-TZP) was explored with the objective of providing defined linear patterns capable of guiding bone-cell response.A nanosecond (ns-) laser was employed to fabricate microgrooves on the surface of 3Y-TZP discs, yielding three different groove periodicities (i.e., 30, 50 and 100 µm). The resulting topography and surface damage were characterized by confocal laser scanning microscopy (CLSM) and scanning electron microscopy (SEM). X-Ray diffraction (XRD) and Raman spectroscopy techniques were employed to assess the hydrothermal degradation resistance of the modified topographies. Preliminary biological studies were conducted to evaluate adhesion (6 h) of human mesenchymal stem cells (hMSC) to the patterns in terms of cell number and morphology. Finally, Staphylococcus aureus adhesion (4 h) to the microgrooves was investigated.The surface analysis showed grooves of approximately 1.8 µm height that exhibited surface damage in the form of pile-up at the edge of the microgrooves, microcracks and cavities. Accelerated aging tests revealed a slight decrease of the hydrothermal degradation resistance after laser patterning, and the Raman mapping showed the presence of monoclinic phase heterogeneously distributed along the patterned surfaces. An increase of the hMSC area was identified on all the microgrooved surfaces, although only the 50 µm periodicity, which is closer to the cell size, significantly favored cell elongation and alignment along the grooves. A decrease in Staphylococcus aureus adhesion was observed on the investigated micropatterns.The study suggests that linear microgrooves of 50 µm periodicity may help in promoting hMSC adhesion and alignment, while reducing bacterial cell attachment.Copyright © 2023 The Authors. Published by Elsevier Inc. All rights reserved.

JTD Keywords: abutment material, alumina toughened zirconia, antibacterial, bacterial adhesion, biofilm growth, cell adhesion, dental implants, hydrothermal degradation, implant surfaces, in-vitro, laser patterning, osseointegration, osteogenic differentiation, part 1, surface topography, y-tzp ceramics, Antibacterial, Antibacterials, Bacteria, Bone, Cell adhesion, Cell culture, Cells adhesion, Ceramics, Chemistry, Degradation resistance, Dental implants, Dental material, Dental materials, Dental prostheses, Human, Human mesenchymal stem cells, Humans, Hydrothermal degradation, Laser patterning, Laser surface, Lasers, Low-temperature degradation, Materials testing, Microscopy, electron, scanning, Nanosecond lasers, Osseointegration, Piles, Scanning electron microscopy, Staphylococcus aureus, Stem cells, Surface analysis, Surface damages, Surface properties, Surface property, Surface topography, Topography, Yttrium, Zirconia, Zirconium

© 2021 Elsevier B.V. Herein, for the first time is described the design of a novel porous zirconia scaffolds manufactured by using polymer-infiltrated ceramic network (PICN) and 3D-printing technologies. Cubic geometry of pieces was obtained by perpendicular layer-by-layer deposition of yttrium-stabilized tetragonal zirconia polycrystal (3Y-TZP) and Pluronic® hydrogel ceramic paste. The specimens were prepared by robocasting assembly with 50% infill and 50% of pores, as feed setup. Bisphenol A glycerolate dimethacrylate (Bis-GMA) and tri(ethylenglycol) dimethacrylate (TEGDMA) copolymer, a well-known biocompatible adhesive, which is widely used in dentistry field, was employed to reinforce the pores of the 3D-printed ceramic structure. The success of the acrylate polymer infiltration above the scaffold surface and among the 3Y-TZP filaments was achieved through previous ceramic functionalization with 3-(trimethoxysilyl)propyl methacrylate (γ-MPS). The well infiltration of the material on pores was evaluated by gravimetry, obtaining a value of 87.5 ± 6.6% of pores covered by the adhesive. Such successful infiltration of methacrylate copolymer had also a positive effect on the mechanical properties of the scaffold material, being the PICN sample that one with the highest elongation resistance. The new system showed reduced bacteria proliferation, over 24 h of incubation with Gram-negative Escherichia coli and Gram-positive Streptococcus salivarius bacteria lines, when compared to the control.

JTD Keywords: acrylate polymer, bacteria colonization, yttrium stabilized zirconia, Acrylate polymer, Bacteria colonization, Robocasting, Yttrium stabilized zirconia