Publications

Laser surface micropatterning of dental-grade zirconia (3Y-TZP) was explored with the objective of providing defined linear patterns capable of guiding bone-cell response.A nanosecond (ns-) laser was employed to fabricate microgrooves on the surface of 3Y-TZP discs, yielding three different groove periodicities (i.e., 30, 50 and 100 µm). The resulting topography and surface damage were characterized by confocal laser scanning microscopy (CLSM) and scanning electron microscopy (SEM). X-Ray diffraction (XRD) and Raman spectroscopy techniques were employed to assess the hydrothermal degradation resistance of the modified topographies. Preliminary biological studies were conducted to evaluate adhesion (6 h) of human mesenchymal stem cells (hMSC) to the patterns in terms of cell number and morphology. Finally, Staphylococcus aureus adhesion (4 h) to the microgrooves was investigated.The surface analysis showed grooves of approximately 1.8 µm height that exhibited surface damage in the form of pile-up at the edge of the microgrooves, microcracks and cavities. Accelerated aging tests revealed a slight decrease of the hydrothermal degradation resistance after laser patterning, and the Raman mapping showed the presence of monoclinic phase heterogeneously distributed along the patterned surfaces. An increase of the hMSC area was identified on all the microgrooved surfaces, although only the 50 µm periodicity, which is closer to the cell size, significantly favored cell elongation and alignment along the grooves. A decrease in Staphylococcus aureus adhesion was observed on the investigated micropatterns.The study suggests that linear microgrooves of 50 µm periodicity may help in promoting hMSC adhesion and alignment, while reducing bacterial cell attachment.Copyright © 2023 The Authors. Published by Elsevier Inc. All rights reserved.

JTD Keywords: abutment material, alumina toughened zirconia, antibacterial, bacterial adhesion, biofilm growth, cell adhesion, dental implants, hydrothermal degradation, implant surfaces, in-vitro, laser patterning, osseointegration, osteogenic differentiation, part 1, surface topography, y-tzp ceramics, Antibacterial, Antibacterials, Bacteria, Bone, Cell adhesion, Cell culture, Cells adhesion, Ceramics, Chemistry, Degradation resistance, Dental implants, Dental material, Dental materials, Dental prostheses, Human, Human mesenchymal stem cells, Humans, Hydrothermal degradation, Laser patterning, Laser surface, Lasers, Low-temperature degradation, Materials testing, Microscopy, electron, scanning, Nanosecond lasers, Osseointegration, Piles, Scanning electron microscopy, Staphylococcus aureus, Stem cells, Surface analysis, Surface damages, Surface properties, Surface property, Surface topography, Topography, Yttrium, Zirconia, Zirconium

Titanium implantation success may be compromised by Staphylococcus aureus surface colonization and posterior infection. To avoid this issue, different strategies have been investigated to promote an antibacterial character to titanium. In this work, two antibacterial agents (silver nanoparticles and a multifunctional antimicrobial peptide) were used to coat titanium surfaces. The modulation of the nanoparticle (≈32.1 ± 9.4 nm) density on titanium could be optimized, and a sequential functionalization with both agents was achieved through a two-step functionalization method by means of surface silanization. The antibacterial character of the coating agents was assessed individually as well as combined. The results have shown that a reduction in bacteria after 4 h of incubation can be achieved on all the coated surfaces. After 24 h of incubation, however, the individual antimicrobial peptide coating was more effective than the silver nanoparticles or their combination against Staphylococcus aureus. All tested coatings were non-cytotoxic for eukaryotic cells.

JTD Keywords: antimicrobial peptide, biomaterials, bone, coatings, performance, ph, resistance, silanization, silver nanoparticles, staphylococcus aureus, Anti-bacterial agents, Antimicrobial peptide, Coated materials, biocompatible, Metal nanoparticles, Reduces bacterial adhesion, Silanization, Silver, Silver nanoparticles, Staphylococcus aureus, Surface properties, Titanium, Titanium functionalization

Since the discovery that nanostructured surfaces were able to kill bacteria, many works have been published focusing on the design of nanopatterned surfaces with antimicrobial properties. Synthetic bone grafts, based on calcium phosphate (CaP) formulations, can greatly benefit from this discovery if adequate nanotopographies can be developed. However, CaP are reactive materials and experience ionic exchanges when placed into aqueous solutions which may in turn affect cell behaviour and complicate the interpretation of the bactericidal results. The present study explores the bactericidal potential of two nanopillared CaP prepared by hydrolysis of two different sizes of alpha-tricalcium phosphate (alpha-TCP) powders under biomimetic or hydrothermal conditions. A more lethal bactericidal response toward Pseudomonas aeruginosa (similar to 75% killing efficiency of adhered bacteria) was obtained from the hydrothermally treated CaP which consisted in a more irregular topography in terms of pillar size (radius: 20-60 nm), interpillar distances (100-1500 nm) and pillar distribution (pillar groups forming bouquets) than the biomimetically treated one (radius: 20-40 nm and interpillar distances: 50-200 nm with a homogeneous pillar distribution). The material reactivity was greatly influenced by the type of medium (nutrient-rich versus nutrient-free) and the presence or not of bacteria. A lower reactivity and superior bacterial attachment were observed in the nutrient-free medium while a lower attachment was observed for the nutrient rich medium which was explained by a superior reactivity of the material paired with the lower tendency of planktonic bacteria to adhere on surfaces in the presence of nutrients. Importantly, the ionic exchanges produced by the presence of materials were not toxic to planktonic cells. Thus, we can conclude that topography was the main contributor to mortality in the bacterial adhesion tests.

JTD Keywords: bactericidal, calcium deficient hydroxyapatite, calcium phosphates, nanopillars, pseudomonas aeruginosa, reactivity, Adhesion, Anti-bacterial agents, Antibacterial, Bacterial adhesion, Bactericidal, Biomaterials, Biomimetics, Calcium deficient hydroxyapatite, Calcium phosphates, Hydroxyapatite, In-vitro, Infections, Nanopillars, Nanostructures, Pseudomonas aeruginosa, Pseudomonas-aeruginosa, Reactivity, Recent progress, Silver, Topography, Transmission

One of the major problems faced by metallic implants is the high probability of bacterial infections, with significant consequences for the patient. In this work, a thermochemical treatment is proposed to obtain silver-doped calcium titanate coatings on the Ti surface to improve the bioactivity of porous 3D-printed Ti structures and simultaneously provide them with antibacterial properties. A complete characterization of the new coating, the study of the ion release and the analysis of its cytotoxicity were carried out together with evaluation of the natural apatite forming in simulated body fluid (SBF). Moreover, the antibacterial properties of the coatings were assessed against Pseudomona aeruginosa and Escherichia coli as gram-negative and Staphylococcus aureus and Staphylococcus epidermidis as gram-positive bacterial strains. Ag ions were integrated into the Ca titanate layer and Ag nanoparticles were formed within the entire 3D Ti surface. Ca and Ag ions were released from both porous and solid samples into the Hanks' solution for 48 h. The treated surfaces showed no cytotoxicity and an apatite layer precipitated on the entire porous surface when the samples were immersed in SBF. The release of Ag from the surface had a strong antibacterial effect and prevented bacterial adhesion and proliferation on the surface. Moreover, the nanostructured topography of the coating resulted also in a reduction of bacterial adhesion and proliferation, even in absence of Ag. In conclusion, the cost-effective approach here reported provided protection against the most predominant bacterial colonizers to the Ti porous implants, while maintaining their bioactivity.

JTD Keywords: 3d-printing, alkaline, antibacterial activity, arthroplasty, bacterial adhesion, biomaterials, generation, ions, nanoparticles, osseointegration, silver, surface-layer, titanium implants, toxicity, 3d-printing, Antibacterial activity, Biomaterials, Porous structures, Silver, Ti metal, Titanium implants

Bacterial colonization plays a key role in dental implant failure, because they attach directly on implant surface upon implantation. Between different types of bacteria associated with the oral environment, Streptococcus sanguinis is essential in this process since it is an early colonizer. In this work the relationship between titanium surfaces modified by shot blasting treatment and S. sanguinis adhesion; have been studied in approached human mouth environment. Bacteria pre-inoculated with routinary solution were put in contact with titanium samples, shot-blasted with alumina and silicon carbide, and adhesion results were compared with those obtained when bacteria were pre-inoculated with modified artificial saliva medium and on saliva pre-coated titanium samples. Our results showed that bacterial adhesion on titanium samples was influenced by culture conditions. When S. sanguinis was inoculated in routinary culture media, colonies forming unities per square millimeter presented an increment correlated with roughness and surface energy, but separated by the type of particle used during shot-blasting treatment; whereas in modified artificial saliva only a relationship between bacteria adhered and the increment in both roughness and surface energy were observed, regardless of the particle type. Finally, on human saliva pre-coated samples no significant differences were observed among roughness, surface energy or particle.

JTD Keywords: S. sanguinis, Bacterial adhesion, Titanium, Artificial saliva, Surface energy, Roughness